Tresna diamantatuen fabrikaziorako matrize metalikoen garapeneansinterizazio-atmosferaren eragina hauts-metalurgiaren bidez
- Gonzalez, Nerea
- Luno-Bilbao, Carmen
- Iturriza, Iñigo
- Iñaki Alegria (ed. lit.)
- Ainhoa Latatu (ed. lit.)
- Miren Josu Omaetxebarria (ed. lit.)
- Patxi Salaberri (ed. lit.)
Editorial: Udako Euskal Unibertsitatea, UEU = Universidad Vasca de Verano
ISBN: 978-84-8438-627-8, 978-84-8438-632-2
Año de publicación: 2017
Título del volumen: Ingeniaritza eta Arkitektura
Tomo: 5
Volumen: 5
Páginas: 126-132
Congreso: Ikergazte. Nazioarteko Ikerketa Euskaraz (2. 2017. Iruñea)
Tipo: Aportación congreso
Resumen
The sintering behaviour of Next 400 prealloyed powder was studied by free sintering. Atmospheres with different hydrogen/nitrogen ratios were used in the sintering cycles. Powder compacts with and without diamond additions were sintered. Uncoated and Ti coated diamonds were used. The interaction between bond/atmosphere/diamond was characterized in terms of density, microstructure and degradation of the diamonds after dissolving the matrix. Diamonds processed under atmospheres with low hydrogen content showed evidence of strong degradation. Both sintering atmosphere and oxygen content of the raw materials are critical parameters in order to protect the surface of the diamonds.